Abstract
Ge epilayers on low temperature (LT) Ge buffer layers were grown by ultrahigh vacuum chemical vapor deposition using the two-step approach. Effects of the growth temperature and the thickness of the low temperature Ge buffers were studied. It was demonstrated that it was unable to obtain flat LT Ge buffers just through lowering the growth temperature due to the ultraslow grow rate that 3D islands formation couldnt be prohibited. However, the rough LT Ge surface was smoothed by subsequent growth at elevated temperature if the LT Ge layer was thick enough and the compressive strain was relaxed largely, and the detrimental Si-Ge intermixing was effectively prohibited as well. When using proper growth conditions for the low temperature Ge buffer, thick Ge epilayer with a low threading dislocation density and a smooth surface was obtained.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.