Abstract
AbstractThis work systematically investigated the crystallization process of NiAl‐layered double hydroxide (NiAl‐LDH) with a Ni(II)/Al(III) ratio of 3 under different crystallization conditions. The results showed that the prepared NiAl‐LDH first exhibits sheet‐like morphology, which transforms into a hexagonal platelet with further growth. The lateral size and thickness of the prepared NiAl‐LDH are ~10–284 nm and ~2–31 nm, respectively. Based on the evolution of morphology, particle size and crystallinity, the growth mechanism of NiAl‐LDH was first proposed. The growth of NiAl‐LDH in the lateral dimension was governed by Ostwald ripening, while the increase in c direction was dominated by oriented particle attachment before precipitation and dissolution equilibrium. Afterward, the growth of NiAl‐LDH was dominated by the oriented particle attachment, leading to further growth of NiAl‐LDH. Moreover, a rotating packed bed (RPB) was first adopted to crystallize NiAl‐LDH. The results show that RPB can greatly enhance the growth of NiAl‐LDH.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.