Abstract
We investigate the growth of ultrathin Cr films on a Au(001) surface and observe that the growth of 1.5 nm thick Cr layers at 290 K, followed by post-annealing at 520 K, results in high-quality epitaxial Cr(001) films with atomically flat large terraces and distinct surface states. Subsequently, these optimized growth conditions are successfully applied to the growth of 1 nm and 3 nm thick Cr films. Magnetic imaging of 1 and 1.5 nm thick Cr(001) films prepared under the optimized growth conditions is performed using spin-polarized scanning tunneling microscopy. Distinct magnetic contrasts featuring a topological antiferromagnetic (TAF) order are observed in both films; however, spin frustration originating from the density of screw dislocations for both films shows a significant difference. The 1.0 nm thick Cr film, which exhibits a clear TAF order with the suppression of a large spin-frustrated area, is suitable for application to spin-electronic devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.