High-quality and large-size ferroelectric single crystal of 1 at.% Mn-doped Na 1/2Bi 1/2TiO 3 has been successfully grown by top-seeded solution growth technique. X-ray fluorescence analysis determines the actual Mn concentration of 0.24 at.% in as-grown Mn-doped Na 1/2Bi 1/2TiO 3 crystal, indicating a very low value of Mn ions diffusion into crystal lattice. Temperature dependence of dielectric constant at different frequencies shows that the dielectric relaxor behavior becomes more distinct after Mn-doping. Moreover, the domain size of Mn-doped Na 1/2Bi 1/2TiO 3 crystal becomes smaller than that of pure Na 1/2Bi 1/2TiO 3 crystal. At room temperature, the [001]-oriented Mn-doped Na 1/2Bi 1/2TiO 3 crystal shows enhanced dielectric, piezoelectric and ferroelectric properties compared with that of pure Na 1/2Bi 1/2TiO 3 crystal. It is clearly demonstrated that Mn-doping is a very effective tool to improve electrical performance of Na 1/2Bi 1/2TiO 3 based single crystals.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.