Abstract
Pore-filling ion exchange membranes are fabricated by complicated and energy-inefficient processes, use of large amounts of polar organic solvents, and optionally post-modification using acid or base. For green fabrication of pore-filling anion exchange membranes (PAEMs), we optimized the process parameters such as pretreatment time, impregnation time, water amount, and photo-polymerization rate of each step using roll to roll (R2R) equipment. Based on these optimized process parameters, a PAEM of 57.5 cm width and 39 μm thickness completely filled with a photo-cured electrolyte polymer was fabricated by aqueous pretreatment and by using an impregnation solution without toxic organic solvents. The impregnation step was conducted along with photo-polymerization at a line speed of 0.3 m/min without repeated impregnation with R2R equipment. The IEC, resistance, and permselectivity of this PAEM were similar to those of handmade PAEMs. The PAEM exhibited chemical stability in the pH range of 0–12. In addition, the reverse electrodialysis stack assembled with these PAEMs exhibited a higher power density than a stack of commercial ion exchange membranes. These results demonstrate that industrial-scale PAEM can be fabricated through a rapid, simple, environmentally friendly, and energy-efficient R2R process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.