Abstract
A transparent conductive graphene film is investigated as front contact in dye-sensitized solar cells (DSSCs), as an alternative to traditional transparent conducting oxides (TCO). The film is composed of poly-crystalline few-layers graphene, covering homogeneously an area of 1cm2, deposited by chemical vapour deposition (CVD) technique on larger area Cu catalyst substrate and transferred on glass. DSSC photoanode is then fabricated, according to consolidated procedure, by sequential casting of TiO2 films through tape casting technique, followed by annealing at 500°C, and sensitization with N719 dye. An outstanding value of photoconversion efficiency as high as 2% is recorded for the best cell, under one sun irradiation (AM 1.5G, 100mWcm−2), which is the highest ever reported for this kind of devices using graphene as front conducting film. Compared to previous results in the literature, the application of a large area continuous graphene film, guaranteed by the CVD deposition, definitely outperforms graphene layers composed by smaller graphene platelets (at micrometer scale). Morphological and electrical characterizations of graphene are reported and the functional performances of the best cell are compared with those obtained from classical DSSC exploiting fluorine-doped tin oxide. Obtained results encourage further investigation of graphene homogeneous thin film as viable alternative to standard TCOs for application in advanced devices, requiring high temperature processing or flexible substrates, incompatible with standard TCO films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.