Abstract
The focus of this study was to determine the mechanisms responsible for the microstructural changes of plasma‐sprayed 7 wt% Y2O3–ZrO2 thermal barrier coatings with annealing from 800° to 1400°C. Mullins's thermal grooving theories have been applied to plasma‐sprayed TBCs to determine the dominant mass transport mechanism at various temperatures. Grain‐boundary groove widths were measured as a function of annealing time and temperature using atomic force microscopy (AFM). The same collection of grains was analyzed after progressive heat treatments. Surface diffusion was found to be the dominant diffusion mechanism at 1000°C, corresponding to the disappearance of intralamellar cracks at that temperature. At 1100°C, both surface and volume diffusion were active. Volume diffusion, found to be the dominant diffusion mechanism at 1200°C and above, was responsible for the sintering of interlamellar pores observed from AFM analysis of a single, progressively heat‐treated interlamellar boundary. Surface roughening was observed to coarsen with increased annealing time and disappear with increased annealing temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.