Abstract
The effects of the grain refinement and eutectic Si modification on tensile properties by using Al-B-Sr master alloys in A356 cast alloy were investigated. Two different master alloys, Al-4%B-1%Sr (4B1Sr) and Al-3%B-3%Sr (3B3Sr), were developed. In microstructure observation, the master alloys were consisted of AlB2, SrB6, AlSrF, KAlF4 and Al4Sr compounds. It should be noted that the α-Al phase also exists in two master alloy. The result showed that the AlB2 area fraction in the 4B1Sr alloy was higher than the 3B3Sr alloy. The 4B1Sr alloy has better efficiencies of α-Al grain refinement and eutectic Si modification than the 3B3Sr alloy, and α-Al grains are refined from 3035 to 312 μm and the eutectic Si is modified from the acicular to fibrous morphology. The tensile properties of 4 wt% treated with 4B1Sr alloy has higher UTS and elongation compared to the treated with 3B3Sr alloy.