Abstract
Low alloy steels serving for a long time at high temperature, e.g., around 500 °C, are very sensitive to temper embrittlement due to segregation of various trace elements at prior austenite grain boundaries and/or carbide/matrix interfaces. This type of segregation in combination with various environmental effects can adversely affect the fracture resistance and fatigue crack propagation rate with subsequent change in fracture morphology of low alloy steels. This article describes the segregation behavior of various elements in 2.25Cr-1Mo pressure vessel steel investigated by AES, FEG-STEM, SEM, and EDS analyses. As confirmed by AES and FEG-STEM, phosphorus is found to be the main embrittling element for isothermal embrittlement. Sulfur and Mo segregation is only evident after longer embrittlement times. In the step-cooling embrittlement, phosphorus is still found to be the main embrittling element, but heavy segregation of sulfur in some isolated intergranular facets was also observed. For P segregation, a Mo-C-P interaction is observed, while sulfur segregation is attributed to site competition between sulfur and carbon atoms.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.