Abstract
High temperature microscopy during oxidation of austenitic stainless steels shows that an increased rate of oxidation is found in a narrow zone along grain boundaries where chromium carbides have been precipitated. This lends support to the chromium-depletion theory of intercrystalline corrosion of these steels. Approximate solution of the appropriate diffusion problem shows good agreement with the experimental results.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.