Abstract
In this study, we present the experimental observation that polycrystalline Mn2+xFe1−xGa (x = −0.2, 0, 0.2, 0.4) compounds can be synthesized to be D019-type (Ni3Sn-type) hexagonal structure with space group P63/mmc. A giant exchange bias field up to 1.32 kOe was achieved in hexagonal Mn2FeGa alloy at 5 K. A cluster glass state is confirmed by ac susceptibility measurement under different driving frequencies. Interestingly, robust horizontal and vertical shifts in magnetic hysteresis loop were simultaneously observed at 5 K under high cooling field up to 90 kOe. The large exchange bias is originated from the large exchange anisotropy between cluster glass phase and ferrimagnetic matrix. The vertical shift is thought to be attributed to the incomplete reversal of frozen cluster spins.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.