Abstract
AbstractThe morphology of Si(001) after carbon deposition of 0.05 to 0.11 monolayers (ML) was investigated in situ by ultrahigh vacuum scanning tunneling microscopy (UHV-STM). The carbon induces a c(4×4)-reconstruction of the surface. In addition, carbon increases the surface roughness compared to clean Si(001) (2×1). In a second step, the influence of the carbon induced restructuring on Ge-island nucleation was investigated. The 3D-growth sets in at considerably lower Ge coverage compared to the clean Si(001) (2×1) surface. This leads to a high density of small though irregularly shaped dots, consisting of stepped terraces, already at 2.5 ML Ge. Increasing the Ge-coverage beyond the critical thickness for facet formation, the dots show { 105 }- facets well known from Ge-clusters on bare Si(001) (2×1). However, they are flat on top with a (001)-facet showing the typical buckled Ge rows and missing dimers. This indicates that the compressive strain is not fully relaxed in these hut clusters.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.