Geopolymers for Space Applications

Abstract

Geopolymers are cementitious materials with exceptional mechanical and physical properties, making them suitable for aerospace applications. Considering their excellent performance, the present investigation aims to develop geopolymers with designed physical properties to address some issues in the aerospace industry. In this sense, the influence of the alkaline activator on the final properties was evaluated. For the development of the geopolymers, sodium hydroxide and sodium metasilicate solutions were preparedto obtain the alkaline activator. The synthesis process also consisted of a mixing stage using a mixer to obtain a homogenous paste. After mixing, the curing process consisted of a first thermal treatment at 60 °C for 4 h to evaporate the excess water, avoid excessive contraction, and promote strength at early ages. Subsequently, the geopolymers were left at rest for 28 days until the final properties were achieved. The influence of the solid-to-liquidratio (S/L) on the microstructure of the geopolymers was evaluated. For this purpose, X-ray fluorescence spectrometry, X-ray diffraction, and infrared spectrometry analyses were performed. The results show that the content of the alkaline activator promotes variations inthe presence of different crystalline phases, which is more noticeable as the S/L ratio increases. Likewise, the infrared spectra display peaks at different wavelengths regarding the variations in elemental composition, which are more evident with the changes in the S/L ratio. In addition, physical studies, such as thermal conductivity and resistance to gamma radiation were conducted for different geopolymer compositions. The results indicate that changes in properties are not too sensitive to compositional variations, although slight modifications exist. Finally, these studies are significant as aerospace-focused materials are directly exposed to this kind of phenomena. The designed geopolymers have to be able to resist and maintain their properties through exposure to any energy.