Generation of hydrogen from aluminum and water – Effect of metal oxide nanocrystals and water quality

Abstract

Metal Oxides nanocrystals such as TiO 2, Co 3O 4, Cr 2O 3, Fe 2O 3, Mn 2O 3, NiO, CuO and ZnO were used as modifiers on the metallic aluminum (Al) powders for the production of hydrogen in deionized water or tap water at room temperature. In particular, the influences of TiO 2 nanocrystals with various crystal sizes on the production of hydrogen from the reaction in tap water under ambient condition were investigated in details. It was found that hydrogen was barely generated from metal Al powders in tap water at 25–45 °C but significantly produced in deionized water above 35 °C without any modifiers. TiO 2, Co 3O 4, and Cr 2O 3 nanocrystals were very effective to promote hydrogen generation from the reaction of Al and deionized water at 25 °C. In addition, while other oxide nanocrystals were ineffective to promote hydrogen generation in tap water, TiO 2 nanocrystals (P90, ∼14 nm in diameter) were found to be highly effective in facilitating the production of hydrogen from the reaction of Al with tap water, comparable to the well-known γ-Al 2O 3. The production of hydrogen over time was found to be dependent on the passive layer of metal Al, where Al(OH) 3 plays an important role during reaction. Pitting is proposed as the major mechanism behind the production of hydrogen in the nanocrystals TiO 2 (P90)-modified Al/tap water system, which is thought to be originated from point defects, and differ considerably from the uniform corrosion model.