Abstract
Abstract In the present work, La 0.75 Ba 0.25 FeO 3 thick films were fabricated by printing the paste (a mixture of La 0.75 Ba 0.25 FeO 3 powders and binder) on an alumina substrate pre-deposited with Ag electrodes. After the printing process, the thick films were annealed at various temperatures. When the La 0.75 Ba 0.25 FeO 3 powders were prepared through annealing at 800 °C for 3 h, the optimal final annealing temperature was about 700 °C for the La 0.75 Ba 0.25 FeO 3 thick film to obtain a large sensing response. The gas sensing properties of La 0.75 Ba 0.25 FeO 3 thick-film sensors depended on the film thickness. The film with thickness of D = 50 μm exhibited the largest response among the four thick films ( D = 30, 50, 70, and 100 μm). La 0.75 Ba 0.25 FeO 3 thick-film sensors could detect acetone and ethanol with very low concentrations (e.g., 5 ppm).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.