Abstract
In this paper, a defect-free polydimethylsiloxane (PDMS)-based composite membrane was synthesized and characterized. The membrane consisted of a thin PDMS film (4 μm) and polyethersulfone (PES) as a support material. At first, a macroporous PES support was prepared by phase inversion method and its thickness, porosity, pore size distribution and surface porosity were determined. PES characterization results confirmed suitability of the support for the composite membrane preparation. Then, PDMS solution, containing crosslinker and catalyst, was cast over the support. Sorption and permeation of C 3H 8, CO 2, CH 4 and H 2 through the synthesized composite membrane were measured at various upstream pressures and based on solution–diffusion mechanism, their diffusion coefficients were calculated. Flory–Huggins (FH) interaction parameters, χ, of the gases with the polymer matrix were calculated based on Flory–Rehner (FR) expression for the crosslinked PDMS membrane and discussed. The concentration-averaged FH interaction parameters of H 2, CH 4, CO 2 and C 3H 8 in the synthesized PDMS membrane were estimated to be 2.526, 0.102, 0.435 and 0.248, respectively. Higher χ values exhibited less favorable interactions between the gas and the membrane and vice versa. Chemical similarity of CH 4 with backbone structure of PDMS, led to the lowest concentration-averaged χ values for CH 4. Increasing feed pressure increased permeability, solubility and diffusion coefficients of bigger gases while decreased those of smaller ones. Hence, C 3H 8/gas ideal selectivity also increased with increasing feed pressure. Only, local effective diffusion coefficient of C 3H 8 increased with increasing penetrant concentration which indicated plasticization effect of C 3H 8 over the range of penetrant concentration studied.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.