Abstract
ABSTRACTA series of ethylene vinyl acetate (EVA)/ethylene‐propylene diene elastomer (EPDM) blends (50/50 ratio) with four types of EVAs were prepared using brabender type batch mixer followed by compression molding. All compression‐molded samples were exposed to gamma radiation at 500, 1000, and 1500 kGy doses and were subjected to mechanical, compression set, thermal and morphological test. The % retention in tensile strength, elongation, and hardness were found higher for higher vinyl acetate (VA) containing radiation aged EVA/EPDM blends. The compression set value was decreased with increase of VA content. The thermal degradation kinetics of high VA containing irradiated blend (EVA40/EPDM) (EVA40 is 40%VA containing EVA) was found slower than those of lower VA containing blend (EVA18/EPDM). The surface morphology for EVA18/EPDM sample was transformed into more irregular one with more cracks and fragmented segments by aging at 1500 kGy dose while surface for EVA40/EPDM sample was found comparatively smooth, fine, and continuous with very few cracks and fragmented parts at similar dose. Thus, from the measured properties and morphology, it was revealed that the degree of degradation of blends kept on decreasing with increase in VA content. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018, 135, 46216.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.