Abstract
The huge availability of volcanic deposits in Mt. Etna volcano and the wide use of volcanic materials as aggregates in local architecture encouraged us to apply them in alkaline environment to produce geopolymeric binders to restore historical buildings of Mt. Etna area. Two clusters of samples for each volcanic precursor (volcanic ash and ghiara paleo-soil) were produced, using 10 and 20% wt. of metakaolin and two different alkaline solutions based on sodium and potassium respectively. A comparative study was made in relation to activators used, focusing on evaluation of polycondensation step (in ATR); chemical and structural characterization (FT-IR); TGA analysis, qualitative XRD analysis and mechanical compressive test after 7 and 21 curing days. ATR results confirmed the occurrence of geopolymerization for all samples; FT-IR analysis showed a higher content of carbonates in potassium-samples, decreasing at increasing of metakaolin content. A low weight lost was recorded in consolidated samples, as well as a partial dissolution of volcanic phases. Higher mechanical compressive strengths for K-samples, reaching 89 MPa as highest value after 21 days, differently to sodium-samples (51 MPa) were recorded, reflecting the porosity of the different specimens.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.