This study investigates the morphological changes induced by femtosecond (fs) laser pulses in arsenic trisulfide (As2S3) thin films and gold-arsenic trisulfide (Au\As2S3) heterostructures, grown by pulsed laser deposition (PLD). By means of a direct laser writing experimental setup, the films were systematically irradiated at various laser power and irradiation times to observe their effects on surface modifications. AFM was employed for morphological and topological characterization. Our results reveal a clear transition threshold between photoexpansion and photoevaporation phenomena under different femtosecond laser power regimes, occurring between 1 and 1.5 mW, irrespective of exposure time. Notably, the presence of a gold layer in the heterostructure minimally influenced this threshold. A maximum photoexpansion of 5.2% was obtained in As2S3 films, while the Au\As2S3 heterostructure exhibited a peak photoexpansion of 0.8%. The study also includes a comparative analysis of continuous-wave (cw) laser irradiation, confirming the efficiency of fs laser pulses in inducing photoexpansion effects.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.