Friction wear property of laser surface processed Ni-based amorphous alloy coatings

Abstract

A Ni–Fe–B–Si–Nb amorphous alloy was deposited on a steel substrate surface via a laser cladding process, and a laser cladding plus laser remelting process. The wear behavior of the laser processed samples and the bulk metallic glass (BMG) sample with the same nominal composition were tested using a pin-on-disc type testing machine. The nano-mechanical properties of the samples were measured with a nano-characterization system. The friction wear tests showed that deep grooves and wear debris were formed on the worn surface of the laser cladded coating, while only shallow grooves for the laser remelted coatings. The friction coefficients of laser remelted coatings and BMG were lower than the laser cladded coating. The wear mass losses of the laser remelted coating were less than the BMG when the laser remelting scanning speed was higher than 6 mm/min. The nano-hardness and elastic modulus of the remelted coating is higher than that of the laser cladded coating. Also, they increase with the increasing laser scanning speed with 1227.9 HV and 277.4 GPa when the remelting scanning speed is 8 m/min. Based on the nano-indentation and friction wear tests results, it was found that the friction wear properties of the laser cladded coating, laser remelted coatings and BMG related well to the ratio of H3/E2. A higher value of H3/E2 can lead to a better wear resistance property.