Abstract
ABSTRACTThe fatigue limit diagram provides the critical condition of non‐failure against fatigue under constant amplitude loading. The fatigue limit diagram is usually considered to give the allowable stress if every stress component is kept within the fatigue limit diagram. In the case of variable amplitude fretting fatigue, however, this study showed that fatigue failure could occur even when all stresses were within the fatigue limit diagram. An example of such a condition is a repeated two‐step loading such as when the first step stress is R=−1 and the second step stress has a high mean value. The reason why such a phenomenon occurs was investigated. A non‐propagating crack was formed by the first step stress even when well below the fatigue limit. The resultant non‐propagating crack functioned as a pre‐crack for the second step stress with a high mean value. Consequently, fatigue failure occurred even when every stress was within the fatigue limit diagram of constant amplitude loading. The fatigue limit diagram obtained in constant amplitude fatigue test does not necessarily guarantee safety in the case of variable amplitude loading in fretting fatigue.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.