Freeze lining formation in continuous converting calcium ferrite slags. II

Abstract

The heat transfer properties of freeze linings generated in laboratory conditions, by industrial calcium ferrite slags from a continuous copper matte flash converting furnace, have been studied in situ in the molten slag using a water cooled probe technique. The measured heat conductivity of the freeze lining formed, estimated from direct measurements in steady state conditions, was 8·0±1·5 W m−1 K−1. The obtained heat conductivity of the freeze lining is 50–100% higher than that of the iron silicate slag freeze linings. The calcium ferrite slag forms a fully crystalline freeze lining. Various ferrites and metallic copper develop the observed high heat conductivity when copper precipitated from the slag during solidification fills the intergranular cavities of the ferrite crystals tightly in forming the freeze lining layer.On a étudié les propriétés de transfert de chaleur de revêtements de gel engendrés en laboratoire par des scories industrielles de ferrite de calcium, à partir d’un four éclair en continu de cémentation de matte de cuivre, dans la scorie fondue en utilisant la technique du capteur refroidi à l’eau. La conductibilité thermique mesurée du revêtement de gel formé, estimée par des mesures directes en conditions de régime permanent, était de 8·0±1·5 W m−1 K−1. La conductibilité thermique obtenue du revêtement de gel est de 50 à 100% plus élevée que celle des revêtements de gel de scorie de silicate de fer. La scorie de ferrite de calcium forme un revêtement de gel entièrement cristallin. Les différentes ferrites et le cuivre métallique développent la conductibilité thermique élevée observée lorsque le cuivre précipité à partir de la scorie pendant la solidification remplit hermétiquement les cavités intergranulaires des cristaux de ferrite dans la couche de revêtement de gel en formation.