Free-standing CuO nanoflake arrays coated Cu foam for advanced lithium ion battery anodes

Abstract

Abstract For lithium ion batteries (LIBs), low electronic conductivity of CuO leads to rapid capacity decay and poor structural stability. Herein, we successfully fabricate three-dimensional CuO nanoflake arrays coated Cu foam by facile and efficient electrochemical oxidation. When being applied as anode material for LIBs, the CuO electrodes deliver stable reversible capacities of 523.9 mA h g −1 at 0.5 A g −1 , 376.1 mA h g −1 at 1.0 A g −1 and 322.7 mA h g −1 at 2.0 A g −1 with high coulombic efficiency (>99%) after 100 cycles. A long cycle life of up to 400 cycles at 2.0 A g −1 is also achieved with the retention capacity of 193.5 mA h g −1 . Moreover, the electrode exhibits excellent rate capability and can regain its original capacities as reversing to the low current densities. Noticeably, on-line differential electrochemical mass spectrometry and in situ Raman measurements confirm the formation of solid electrolyte interface film and the conversion mechanism for the CuO electrodes, respectively. The superior lithium storage performance can be attributed to the favorable nanoflake structures with high surface area and the perfect electrical contact between CuO and Cu substrate.