Abstract
Delamination is the common failures of composite material attributed to various reasons, most importantly the potential stiffness degradation leading to small flaws and subsequently theypropagate, and it becomes essential to characterize the new materials for interlaminar fracture. For the present study Carbon /epoxy system of IM7/8552 was investigated under mode I and mode II loading. Material was formed into unidirectional laminates with Teflon inserts at its mid length. The specimens were machined according to ASTM standards, Tests were executed on a quasi-static Intron 8225, with load control at 5 mm/ min and 2 m/min for the mode -I and mode-II respectively. The strain energy release rate was found to be GIC=0.266 kJ/m2 and GIIC=0.687 kJ/m2. Fiberbridging was prominently absent in the DCB samples Examination of the fracture surface by SEM at SAIF, in IIT{M) and the nature of the fracture surface revealed the typical failure mechanism pertaining to mode-I and mode-II failuremechanisms.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Innovative Technology and Exploring Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.