Abstract
The processes of defect formation in silicon following high-energy ion implantation were studied using the Hall effect and IR absorption spectroscopy. Point radiation defects were found far beyond the region of typical ion projected ranges. It is suggested that the defects were formed as a result of diffusion of interstitials and vacancies from the implanted region further into the substrate. The efficiency of the formation of these defects was found to decrease with increase of the mass of implanted ions and is thought to be related to the increase in concentration of the interstitial and vacancy traps.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.