Abstract
For the Pd-Ta system characterized by a negative heat of formation of −78 kJ/mol, 200 keV xenon ion beam mixing with nano-sized Pd-Ta multilayered films was conducted to study the non-equilibrium phase formation. The results showed that uniform amorphous alloys can be formed within a composition range of 25 at%–78 at% Ta, which falls in the maximum possible amorphization range of 22 at%–80 at% Ta predicted by the empirical model. Moreover, two metastable crystalline phases both of FCC structure, yet with different lattice constants were obtained. Interestingly, a self-assembled fractal pattern was observed in the Pd52Ta48 multilayered films after irradiation to a dose of 1×1015 Xe+/cm2 and its dimension was determined to be 1.75±0.05. The possible mechanisms for the formation of amorphous and metastable crystalline phases as well as for the growth of the fractal pattern were discussed.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.