Abstract
The effect of the concentration of alloying components on the crystallization of amorphous (Fe73Si13B9)1 – x – yNbxCuy and (Co70Si12B9)1 – x – yFexNby alloys has been studied by X-ray diffraction and transmission electron microscopy in a wide composition region. The formation of the bcc structures in both the alloy groups is shown to be substantially dependent on the alloying component concentrations. The bcc phase is found to form in the cobalt-based alloys in the concentration region, where it was not observed before. In the cobalt-based alloys, the bcc phase appears at a niobium concentration higher than 1 at % and the average bcc nanocrystal size varies from 40 nm (at 1 at % Nb) to 14 nm (at 5 at % Nb). In the Fe-based alloys, nanocrystals with the bcc lattice form at the copper concentrations of 0.45–1 at %, and the average nanocrystal size is dependent on the alloy composition and varies in the range 16–24 nm. The causes of the concentration dependence of the formation of nanostructures in these alloys are discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.