Abstract
The formation of amorphous interlayers (a-interlayers) by solid-state diffusion in ultrahigh-vacuum-deposited polycrystalline Ti thin film on germanium and epitaxial Si1−xGex (x=0.3, 0.4, and 0.7) alloys grown on (001)Si has been investigated by transmission electron microscopy and Auger electron spectroscopy. Amorphous interlayers, less than 2 nm in thickness, were observed to form in all as-deposited samples. The growth of the a-interlayers was found to vary nonmonotonically with the composition of Si–Ge alloys in annealed samples. On the other hand, the formation temperature of crystalline phase was found to decrease with the Ge content. The results are compared with those of the Ti/Si system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.