Abstract
Bulk metallic glass (BMG) formation was explored in the Fe-B-Si-Nb alloy system though combined use of the atomic cluster line approach and the minor alloying strategy. The basic ternary compositions in the Fe-B-Si system were determined by the intersection points of two cluster lines, namely, Fe-B cluster to Si and Fe-Si cluster to B. 3at%–4at% Nb was added to the quaternary Fe-B-Si-Nb alloy. The casting experiments revealed that good glass-forming ability (GFA) occurred at the (Fe73.4Si8.2B18.4)96Nb4 composition, and 3-mm diameter BMG samples were made. The glass transition temperature (T g), crystallization temperature (T x), and supercooled liquid region (ΔT x=T x−T g) of this BMG were measured to be 866, 889, and 23 K, respectively. The BMG shows a high Vickers hardness of about Hv 1164, a Young’s modulus of 180 GPa, and a good corrosion resistance in the solutions of 1 mol/L HCl and 3wt% NaCl.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.