Abstract
A test method for measuring formaldehyde from urea-formaldehyde (UF) resins at high temperature was developed and used to assess the influence of the reaction pH on the formaldehyde emission and heat stability of the cured resins. Additionally, solid-state13C CP/MAS nuclear magnetic resonance (NMR) techniques were used to investigate the structure of cured UF resins before and after high temperature heating. Formaldehyde emissions during the cure were related to the UF resins' methylol group content. The heat stability of cured UF resins synthesized under strongly acidic conditions was much higher than that of the other resins, which were prepared in weakly acidic and alkaline media. Solid-state13C CP/MAS NMR spectra showed that formaldehyde emission from cured UF resins after heating is mainly ascribable to decreased methylol groups and dimethylene ether linkages. Significantly, it was revealed that uron structures characteristically found in the cured UF resin synthesized under strongly acidic medium indicated high heat stability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.