Fluoride varnishes supplemented with nano-sized sodium trimetaphosphate reduce enamel erosive wear in vitro

Abstract

ObjectiveTo evaluate the effect of fluoride (F) varnishes with sodium trimetaphosphate (TMP) on erosive tooth wear (ETW) in vitro. MethodsEnamel blocks (n = 100) were divided into 5 experimental groups (n = 20/group): Placebo (Pla - without F/TMP); 5 % NaF (NaF); 5 % NaF + 5 % micrometric TMP (NaF+5 %MICRO); 5 % NaF + 2.5 % nano-sized TMP (NaF+2.5 %NANO), and 5 % NaF + 5 % nano-sized TMP (NaF+5 %NANO). Blocks received a single varnish application (6 h contact), and were submitted to 4 daily erosive challenges (ERO, 0.05 M citric acid, pH 3.2, 90 s, under agitation), for 5 days. After ERO, half of the blocks (n = 10/group) were subjected to brushing abrasion (ERO+ABR). Profilometry, surface hardness (SH), and cross-sectional hardness (ΔKHN) were determined. The data were submitted to 2-way ANOVA and Fisher's LSD test (p < 0.05). ResultsEnamel wear was significantly lower for ERO compared with ERO+ABR for all varnishes tested (p < 0.001), following the pattern NaF+5 %NANO < NaF+5 %MICRO < NaF < NaF+2.5 %NANO < Pla (both for ERO and ERO+ABR). The highest SH loss was observed for Pla and the lowest for NaF (ERO) and NaF+2.5 %NANO (ERO+ABR), without significant differences among NaF+2.5 %NANO, NaF, and NaF+5 %MICRO. The highest ΔKHN values were observed for NaF+5 %MICRO and NaF+5 %NANO at 5–30 µm, with less marked differences among the groups at 30–70 µm (ERO and ERO+ABR). ConclusionsThe addition of TMP to F varnishes significantly improves protection against ETW in vitro. The use of 5 % nano-sized TMP further enhances such effects. Clinical significanceF varnishes containing TMP can reduce enamel loss caused by ERO or ERO+ABR.