Abstract
3-point flexural fatigue and Mode I interlaminar fracture tests were done to study the fatigue life and fracture toughness of nanoclay added carbon fiber epoxy composites. Fatigue life data was analyzed using Weibull distribution function, validated with Kolmogorov-Smirnov goodness-of-fit, and predicted by combined Weibull and Sigmoidal models, respectively. The nanophased samples showed more than 300% improvement in mean and predicted fatigue life. At 0.7 stress level, the nanophased samples passed the ‘run-out’ fatigue criteria (106 cycles), whereas, the neat samples failed much earlier. The interlaminar fracture toughness of nanophased samples was also enhanced significantly by 71% over neat samples. Optical and scanning electron microscopic images of the nanophased fractured samples revealed certain features that improved the respective fatigue and fracture properties of the composites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.