Abstract
The magnetic properties and magnetic structure of an as-prepared Mn(Co0.96Fe0.04)Ge sample has been investigated by powder neutron diffraction as well as X-ray diffraction and magnetisation measurements. The sample has a ferromagnetic structure in the low-temperature orthorhombic phase and a magneto-structural transition at 299 (1) K to the high-temperature paramagnetic hexagonal phase. This transition occurs at a higher temperature than for as-prepared (Mn0.96Fe0.04)CoGe (TM = 239 (1) K). Increased occupancy by Fe of the Co (4c) site rather than the Mn (4c) site results in this smaller suppression of the structural transition temperature away from that of undoped MnCoGe. It was found that chemical pressure increased the Curie temperature TCorth in the orthorhombic phase from 355 (5) K in Mn(Co0.96Fe0.04)Ge to 379 (6) K in MnCoGe. Mn(Co0.96Fe0.04)Ge exhibits a large magnetocaloric effect around the magneto-structural transition, −ΔSmpeak = 11 (2) J kg−1 K−1 and RC = 187 (30) J kg−1 with μ0ΔH = 5 T. The magneto-structural transition is a first order transition as demonstrated by master curve analysis.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.