Abstract
Well-aligned TiO 2/Ti nanotube arrays were synthesized by anodic oxidation of titanium foil in 0.5 wt.% HF in various anodization voltages. The images of filed emission scanning electron microscopy indicate that the nanotubes structure parameters, such as diameter, wall thickness and density, can be controlled by adjusting the anodization voltage. The peaks at 25.3° and 48.0° of X-ray diffraction pattern illuminate that the TiO 2 nanotube arrays annealed at 500 °C are mainly in anatase phase. The filed emission (FE) properties of the samples were investigated. A turn-on electric field 7.8 V/µm, a field enhancement factors approximately 870 and a highest FE current density 3.4 mA/cm 2 were obtained. The emission current (2.3 mA/cm 2 at 18.8 V/µm) was quite stable within 480 min. The results show that the FE properties of TiO 2/Ti have much relation to the structure parameters.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.