η-fiber microstructure and texture evolutions in ultra-thin silicon steel

Abstract

0.08mm ultra-thin silicon steel is prepared with 0.30mm commercial grain-oriented silicon steel as raw material, and the evolutions of η-fiber microstructure and texture are investigated with emphasis. During rolling deformation, initial Goss orientation shows crystal rotation to {111 }<112> orientation. With the increase of rolling reduction, the retention of Goss orientation is reduced and more observed near the sheet surface. For initial deviated Goss oriented grains, {111}<112> and η-fiber oriented areas are also observed in 0.08mm rolled sheet, while the accuracy and concentration of these two components are decreased. During annealing, η-fiber nucleation superiority in γ-fiber deformed regions is significant, and thus contributes to strong η-fiber recrystallization texture. When the rolled sheets are heated at 800 °C for 15 min, strong η-fiber recrystallization texture and uniform microstructure is beneficial for the magnetic properties of ultrathin silicon steel sheets.