Abstract
We report the preparation and characterization of vanadium substituted four-layer Aurivillius compound Bi5Fe1.5V0.5Ti2O15 using spin coating method. Ferroelectricity in the prepared films are confirmed from the well saturated polarization vs electric field (P-E) loops having remnant polarization (2 Pr) around 12.94 µC/cm2 at room temperature. In addition, low temperature P-E measurements show a decrease in Pmax and 2 Pr, which is attributed to the stabilization of defect dipole complexes and domain pinning, as seen in bismuth-based ferroelectrics. Additionally, this decrease in polarization is accompanied by an increase in imprint, confirming the presence of defect dipoles manifested as internal fields.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.