Abstract
The purpose of this study was to test the hypothesis that the pulp medication ferric sulphate (FS) may remain on primary dentin, affecting its microchemical structure and the bond strength of adhesives to primary dentin. The effects of FS and pre-bonding conditioning (37% phosphoric acid [PA] for 15 s or a self-etching primer, with or without the use of 2% chlorhexidine [CHX]) on FS-treated primary dentin were characterized using optical microscopy with Masson's and Perls' stains, variable-pressure SEM/energy-dispersive x-ray spectroscopy (VP-SEM/EDS), Fourier transform infrared spectroscopy (FT-IR), and x-ray diffraction. Ferric sulphate was applied for 30 s or 1 h for microchemical analysis. The adhesive interface and the bond strength were studied by VP-SEM/EDS and the μTBS test (1 mm2 bars, crosshead speed 0.5 mm/min), respectively. The study groups were: etch-and-rinse (E&R, Excite) adhesive (group 1); FS+E&R (group 2); FS+CHX+E&R (group 3); self-etching (SE, Adper Scotchbond) adhesive (group 4); FS+SE (group 5); FS+CHX+SE (group 6). Ferric sulphate application produced demineralization, gypsum formation, and adsorption of Fe on the dentin surface, and it modified the collagen structure of primary dentin. There were no effects of FS on bond strength of the tested etch-and-rinse adhesive system. FS slightly reduced the bond strength between the primary dentin and the SE adhesive, and the values were not restored by CHX (group 4 = 17.58 ± 5.52 MPa > group 5 = 14.26 ± 7.08 MPa = group 6 = 13.96 ± 4.87 MPa). Ferric sulphate alters the microchemical structure of primary dentin and can impair the adhesive strength of some self-etching adhesives.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.