Abstract
FeMn alloy is a promising biodegradable metal due to its high strength and biocompatibility, but the inadequate degradation rate and poor surface performance impede its further development. To overcome the drawbacks, femtosecond laser surface modification was used to establish nano-ripple structure on the Fe-30Mn alloy surface in this work. After laser texturing, typical nano-ripple structures were established on the alloy surfaces. With the increase of laser average line fluence from 10 to 30 J cm−2, the nano-ripple period decreased and vertical sinuous grooves were formed on the surface, resulting in a high roughness value and a hydrophobic surface. Compared with the polished sample, the nano-ripple structure surface exhibited significant improvement of the actual biodegradation rate. Further, in vitro cell counting kit-8 test showed that the laser surface modification had few effects on the cytocompatibility of Fe-30%Mn alloy. The results indicate its great potential for physical surface modification of biodegradable metals.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.