Abstract
The temperature dependences of the specific contact resistance of silicon ρc with a doping step are measured experimentally and described theoretically. The measurements are performed in the temperature range from 4.2 to 380 K. It is established that the contacts of the studied Au–Ti–Pd–n+–n-Si structures are ohmic. It is shown that minimal ρc is implemented at T = 75 K. Its value rises both with a decrease in temperature (due to the freezing effect) and with an increase in temperature (due to the electron-enriched layer at the boundary with the bulk material). It is established that the bulk electron concentration strongly decreases in the near-contact region in a layer with a thickness on the order of one micron due to the compensation of silicon by deep acceptors appearing because of the formation of a rather high vacancy concentration during stress relaxation and the appearance of a high dislocation density, as well as due to their diffusion from the contact after heating to 450°C. The data on the occurrence of vacancy-type defects are confirmed by X-ray measurements. The dislocation density in the studied structures is also estimated from X-ray measurements.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.