Abstract
In this study, the fatigue life of aluminum alloys (7001-T6) was predicted with shot peening at various temperatures. Surface treatment with shot peening steel balls is a mechanism for reducing damage. An experimental investigation was conducted to find the degree of fatigue accumulation for AA7001-T6 under rotational bending loading and stress ratio R = −1. The experiments were conducted at RT (25 ℃), 330 ℃, and SP + 330 ℃ temperatures. A modified damage stress model that considers damage at various load levels was recommended for forecasting the fatigue life under high temperatures. The model and experimental results were compared to determine the most damage (Miner’s rule). The experimental results of the fatigue life indicated that the increased testing temperature reduced the fatigue life. However, using shot peening at high temperatures increased the fatigue life by 8% when loading sequence L-H and 10% when loading sequence H-L. The results showed a satisfactory degree of safety for the present model. Nevertheless, Miner’s model featured two models: one for low–high loading and high-low loading. The results were proper for prolonging fatigue life.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.