Abstract
This paper describes the fatigue crack propagation behavior of rolled and extruded AZ31B magnesium alloys (grain size: approximately 20 and 15 mm, respectively). Fatigue crack propagation tests were performed on center cracked plate tension specimens at a stress ratio of R ¼ 0:1 and a frequency of 10 Hz at room temperature. Loading axes were parallel to the rolling and extrusion directions; fatigue cracks propagated parallel to the transverse direction (L-T specimen of rolled AZ31B), parallel to the short transverse direction (L-S specimen of rolled AZ31B), and perpendicular to the extrusion direction (E-R specimen of extruded AZ31B). The crack growth rate (da=dN) of the L-S specimen was approximately 10 times lower than that of the L-T specimen in the examined stress intensity factor (� K) range. Fracture surfaces of the L-T and L-S specimens showed many steps parallel and perpendicular, respectively, to the macroscopic crack growth direction. The plot of the da=dN
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.