Abstract
This paper describes the fatigue crack propagation behavior of extruded AZ31B magnesium alloys (average grain size: approximately 15 and 119 μm, respectively). Fatigue crack propagation tests were performed on center cracked tension (CCT) specimens at a stress ratio of R=0.1 and a frequency of 10 Hz at room temperature. Loading axis was parallel to the extrusion direction; crack face was perpendicular to basal plane of each grain. The crack growth rate (da/dN) of the coarse-grained specimen was approximately 5 times higher than that of the fine-grained specimen. Fracture surfaces of the fine-grained and coarse-grained specimens showed various directional steps independent of macroscopic crack growth direction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.