Abstract
The influence of residual stress on fatigue crack growth was experimentally and analytically investigated for surface crack. Fatigue tests were performed on straight pipe components of low-carbon steel having a circumferential inner surface crack in laboratory air environment. Some of the test pipes had been subjected to special heat treatments so as to have compressive or tensile residual stresses along the inner surface. The results show that the compressive residual stress remarkably suppresses the surface crack growth while the tensile residual stress doesn't accelerate the crack growth very much. The crack growth analyses were conducted by the application of power relationship between Δ K and da dN . The stress intensity factors due to the non-linear stress field were calculated by the weight function method. The analyses resulted in a confirmation of the behavior of the crack growth observed in the experiments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.