Abstract

This paper presents experimental results from cyclic crack propagation tests performed on sandwich specimens with glass/epoxy face sheets and Poly Vinyl Chloride (PVC) foam cores using the G-controlled cyclic energy release rate (ΔG) test procedure. The face material was tested in tension, compression and shear to determine in-plane and out-of-plane mechanical properties, such as Young’s modulus, Poisson’s ratio and shear modulus. These properties were then used in an analytical model of the mixed-mode bending sandwich specimen to calculate compliance and energy release rate. Finite element analysis was used to determine the mode-mixity of the crack loading. Experimental crack growth cyclic tests were carried out on pre-cracked mixed-mode bending sandwich specimens with H45, H100 and H160 PVC foam cores under two mode-mixities (mode I and mode II dominant). Post-mortem analysis was performed on tested specimens, highlighting the influence of mode mixity and foam density on the crack path. Crack propagation diagrams showing da/dN versus ΔG curves were obtained to establish the Paris-Erdogan relation for each material combination tested at the two mode-mixities. Results showed constant crack growth rates for all the materials tested and revealed the influence on mode-mixity on crack propagation speed and foam density (higher foam density, slower crack propagation).

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.