Abstract
Fatigue and fracture tests of piping models with flaws in the inner surface were carried out to investigate the fatigue crack growth, coalescence of multiple cracks and fracture behavior. Two straight test pipes with and without weldment in the test section of AISI type 304L stainless steel were tested under almost the same test conditions by imposing moment loads. Three artificial defects were machined in the inner surface of the test section of the test pipes and the fatigue test was performed until the cracks coalesced and grew through the thickness. Subsequently, a static load was imposed on the test pipe which contained a large crack in the test section. The fatigue test results are compared with an analytical crack growth behavior predicted by the method described in the Section XI of ASME Code, and show slower crack growth than that of the prediction. From the fracture test results, it is found that the test pipes can endure considerably high load.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.