Abstract
In-plane shear strength (IPSS) of a two-dimensional carbon fiber reinforced silicon carbide composite (C/SiC) was measured by compression of double-notched specimens (DNS) from room temperature to 1873 K. The result indicates that the compression of DNS is an effective method to measure IPSS of C/SiC. A significant dependence of IPSS on temperature was found for C/SiC. IPSS increases with increasing temperature up to 1273 K, and then decreases when the temperature was higher. The main failure modes under the shear loading contain matrix cracking, delamination and pullout of fibers and fiber bundles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.