Abstract
Aluminum bond pads on semiconductor chips play an important role in chips functionality and reliability. Bond pad peeling during wire bonding process results in yield reduction. The failure mechanisms of the peeling must be identified so that potential reliability problem of poor bond pad adhesion can be avoided. In this work, FIB, SEM, EDX, and AFM are used to identify the root causes of the peeling. The possible root causes are found to be the presence of an extra layer of thickness of 0.14 μm and the poly-silicon surface roughness asperity due to prolonged BOE etching time.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IEEE Transactions on Components, Packaging, and Manufacturing Technology: Part A
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.