Abstract
Reduced graphene oxide-based films were prepared to assess their effects as gas barriers on the stability of organic photovoltaic (OPV) devices. The direct spin-casting of a graphene oxide suspension onto an aluminum electrode was performed to encapsulate the associated OPV device with a reduced graphene oxide film. The lifetime of the OPV device after the reduction process was found to be increased by a factor of 50. The gas barrier properties of a graphene oxide layer are closely related to its surface roughness and dispersibility. Furthermore, these gas barrier properties can be enhanced by controlling the thermal reduction conditions. The thermal reduction of a graphene oxide film at a low heating rate results in a low water vapor permeability, only 0.1% of that of an as-prepared polyethylene naphthalate film. These results indicate that the dispersibility, surface roughness, and reduction conditions of a graphene oxide film significantly influence its gas barrier performance. Further investigations of the reduction of graphene oxide films are expected to enable further improvements in performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.