Abstract
Facile and scalable fabrication of α-Fe2O3 photoanodes using a precursor solution containing FeIII ions and 1-ethylimidazole (EIm) in methanol was demonstrated to afford a rigidly adhered α-Fe2O3 film with a controllable thickness on a fluorine-doped tin oxide (FTO) substrate. EIm ligation to FeIII ions in the precursor solution brought about high crystallinity of three-dimensionally well-interconnected nanoparticles of α-Fe2O3 upon sintering. This is responsible for the 13.6 times higher photocurrent density (at 1.23 V vs reference hydrogen electrode (RHE)) for photoelectrochemical (PEC) water oxidation on the α-Fe2O3 (w-α-Fe2O3) photoanode prepared with EIm compared with that (w/o-α-Fe2O3) prepared without EIm. The w-α-Fe2O3 photoanode provided the highest charge separation efficiency (ηsep) value of 27% among the state-of-the-art pristine α-Fe2O3 photoanodes, providing incident photon-to-current conversion efficiency (IPCE) of 13% at 420 nm and 1.23 V vs RHE. The superior ηsep for the w-α-Fe2O3 photoanode is attributed to the decreased recombination of the photogenerated charge carriers at the grain boundary between nanoparticles, in addition to the higher number of the catalytically active sites and the efficient bulk charge transport in the film, compared with w/o-α-Fe2O3.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.