Abstract
High‐toughness and high‐strength lead zirconate titanate (PZT) composites that contain fine silver particles were successfully fabricated at low sintering temperatures. Addition of silver to a PZT matrix did not result in unwanted reaction phases; however, some silver diffused toward the perovskite crystal structure. A small quantity of silver accelerated the sinterability of the PZT composites. The formation of oxygen vacancies due to the partial substitution of silver appeared to enhance the sinterability of the PZT. Fracture toughness depended on the size and degree of sphericity of the silver particles, and SEM observations on crack propagation suggested that the toughening mechanism in the PZT/Ag composites involves crack bridging resulting from the ductile behavior of silver particles. It is proposed that high fracture strength in PZT/1 to 5 vol% Ag composites results from the relaxation of transformation‐induced internal stress by the silver particles.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call